The study is referred to the thermodynamic activities of Fe in alloys of Ni-Fe, of Ni in alloys of Cu-Ni and of Fe in alloys of Cu-Ni-Fe at temperatures 800o-1000oC. From the study arose the following : 1) In the alloys of Ni-Fe,the according to Raoult activities of Fe, present small negative declinations, from the ideal behavior up to 50% grammatonic concentration Fe. 2) In the alloys of Cu-Ni, the according to Raoult activities of Ni present potent positive declinations to all the scale of concentration, 3) In the alloys Cu-Ni-Fe, the according to Raoult activities of Fe, present positive declinations, particularly when the concentration in Cu is increased. Finally, all the alloys that were examined, approached the ideal behavior when the temperature was increasing.
Μελέτη των θερμοδυναμικών ενεργοτήτων του Fe σε κράματα Ni-Fe, του Ni σε κράματα Cu-Ni και του Fe σε κράματα Cu-Ni-Fe σε θερμοκρασίες 800-1100 C.
Α) Στα κράματα Ni-Fe , οι κατά Raoult ενεργότητες του Fe παρουσιάζουν μικρές αρνητικές αποκλίσεις από την ιδανική συμπεριφορά μέχρι και 50% της γραμμοατομικής συγκέντρωσης του Fe.
Β) Στα κράματα Cu-Ni , οι κατά Raoult ενεργότητες του Ni παρουσιάζουν ισχυρές θετικές αποκλίσεις σε όλη την κλίμακα συγκέντρωσης.
Γ) Στα κράματα Cu-Ni-Fe, οι κατά Raoult ενεργότητες του Fe, παρουσιάζουν θετικές αποκλίσεις, ιδιαιτέρως όταν αυξάνεται η περιεκτικότητα σε Cu.
Τέλος όλα τα κράματα που εξετάσθηκαν πλησίαζαν την ιδανική συμπεριφορά όταν αυξανόταν η θερμοκρασία.